***三菱高流动POM Iupital F30-73R1低气味排放
|
Density |
1.41 |
g/cm? |
ISO 1183 |
|
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) |
27 |
g/10 min |
ISO 1133 |
|
Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) |
23 |
cm?/10min |
ISO 1133 |
|
Molding Shrinkage - Flow (3.00 mm) |
2.0 |
% |
Internal Method |
|
Water Absorption - 60% RH (23°C) |
0.22 |
% |
Internal Method |
| Mechanical |
Nominal Value |
Unit |
Test Method |
|
Tensile Modulus |
2900 |
MPa |
ISO 527-2/1 |
|
Tensile Stress (Yield) |
64.0 |
MPa |
ISO 527-2/50 |
|
Tensile Strain |
|
|
ISO 527-2/50 |
|
Yield |
7.5 |
% |
|
|
Break |
26 |
% |
|
|
Flexural Modulus 3 |
2700 |
MPa |
ISO 178 |
|
Flexural Stress 3 |
91.0 |
MPa |
ISO 178 |
| Impact |
Nominal Value |
Unit |
Test Method |
|
Charpy Notched Impact Strength (23°C) |
6.0 |
kJ/m? |
ISO 179 |
|
Charpy Unnotched Impact Strength (23°C) |
150 |
kJ/m? |
ISO 179 |
| Thermal |
Nominal Value |
Unit |
Test Method |
|
Heat Deflection Temperature |
|
|
|
|
0.45 MPa, Unannealed |
156 |
°C |
ISO 75-2/B |
|
1.8 MPa, Unannealed |
100 |
°C |
ISO 75-2/A |
|
Melting Temperature |
166 |
°C |
ISO 11357-3 |
| Flammability |
Nominal Value |
|
Test Method |
|
Flame Rating (0.8 mm) |
HB |
|
UL 94 |
 |
POM注塑工艺特性与工艺参数的设定
1、POM也是典型的热敏性塑料，240℃下会严重分解。在210℃下，停留时间不能超过20min；即使在190℃下，停留时间也不能超过1h。因此注塑时，在保证物料流动性的前提下，应尽量选用较低的成型温度和较短的受热时间。
2、POM具有明显的熔点，均聚POM为175℃、共聚POM为165℃。成型时，料筒温度的分布：前段190～200℃，中段180～190℃，后段150～180℃，喷嘴温度为170～180℃。对于薄壁制品，料筒温度可适当提高些，但不能超过210℃
3、POM吸湿性小，加工前树脂可不干燥。必要时，可在90～100℃下，干燥2～4h。
4、POM的熔体粘度对剪切速率敏感。因此，要提高熔体流动性，不能单用提高温度，也要从提高注射速率和注射压力着手。大浇口、厚壁短流程、小面积的制品，注射压力为40～80MPa；一般制品为100MPa左右。小浇口、薄壁长流程、大面积的制品，注射压力较高，为120～140MPa 。
5、模具温度通常控制在80～100℃，对薄壁长流程