原包三菱低气味高抗冲POM Iupital FU2010R2
|
Density |
1.38 |
g/cm? |
ISO 1183 |
|
Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) |
6.0 |
cm?/10min |
ISO 1133 |
| Mechanical |
Nominal Value |
Unit |
Test Method |
|
Tensile Stress (Yield) |
51.0 |
MPa |
ISO 527-2/50 |
|
Tensile Strain |
|
|
ISO 527-2/50 |
|
Yield |
10 |
% |
|
|
Break |
50 |
% |
|
|
Flexural Modulus 3 |
2000 |
MPa |
ISO 178 |
|
Flexural Stress 3 |
70.0 |
MPa |
ISO 178 |
| Impact |
Nominal Value |
Unit |
Test Method |
|
Charpy Notched Impact Strength (23°C) |
9.0 |
kJ/m? |
ISO 179 |
|
Charpy Unnotched Impact Strength (23°C) |
No Break |
|
ISO 179 |
| Thermal |
Nominal Value |
Unit |
Test Method |
|
Heat Deflection Temperature (1.8 MPa, Unannealed) |
87.0 |
°C |
ISO 75-2/A |
|
Melting Temperature |
166 |
°C |
ISO 11357-3 |
| Flammability |
Nominal Value |
|
Test Method |
|
Flame Rating (0.8 mm) |
HB |
|
UL 94 |
用途
多聚甲醛为高甲醛含量的固态甲醛，呈固体颗粒状、便于贮存和运输。在较高的温度下能变成甲醛蒸气，易于代替高浓度甲醛参与各种反应，有利于化工、制药等化学合成及其他工业领域的应用，特别是在要求使用无水甲醛作原料的合成方面，用途***。主要有以下几方面（1）农药：合成乙草胺、丁草胺和草甘膦等；（2）涂料：合成***汽车用漆；（3）树脂：合成脲醛树脂、酚醛树脂、聚缩醛树脂、蜜胺树脂、离子交换树脂等及各种粘合剂；（4）造纸：合成纸张增强剂； （5）铸造：翻砂脱膜剂、合成铸造粘合剂；（6）养殖业：薰蒸消毒剂。（7）有机原料：用于制备季 戊 四 醇、三羟甲基丙烷、甘油、丙烯酸、丙烯酸甲酯、甲基丙烯酸、N－羟基甲基丙烯酰胺、烷基苯酚、甲基乙烯基酮等。（8）其他：医药及消毒。